SACW 410 NiMoN | Certilas: The filler metal specialist

Go Back

productspecificaties
Verpakkingen
vraag offerte

Type

Tubular wire based on a 13% Chromium and 4% Nickel deposit stabilized with Niobiumn.

Higher productivity, higher deposition rates and improved wetting properties compared to solid wires with comparable analysis. Attractive bead appearance without slag residues. Hard facing alloy with excellent thermo shock resistance and increased hardness due to additions of Vanadium and Niobium. Best to be used with FL 915 or FL 8111 welding flux.

Not required

classification

AWS

A 5.9: ER410NiMo

EN ISO

14700: T Fe7

Toepassingen

Cladding wear resistant overlays in steel mills and applications of the same kind.

Type

Tubular wire based on a 13% Chromium and 4% Nickel deposit stabilized with Niobiumn.

Toepassingen

Cladding wear resistant overlays in steel mills and applications of the same kind.

Eigenschappen

Higher productivity, higher deposition rates and improved wetting properties compared to solid wires with comparable analysis. Attractive bead appearance without slag residues. Hard facing alloy with excellent thermo shock resistance and increased hardness due to additions of Vanadium and Niobium. Best to be used with FL 915 or FL 8111 welding flux.

Classificatie

AWS

A 5.9: ER410NiMo

EN ISO

14700: T Fe7

Geschikt voor

13%Cr - 4%Ni - 0,5%Mo Steel

1.4000, 1.4001, 1.4002, 1.4313, 1.4317, 1.4407, 1.4413, 1.4414,

GX4CrNi13-4, X3CrNiMo13-4, GX5CrNiMo13-4, GX4CrNiMo13-4, X 6 Cr 13, X 7 Cr 14, X 6 CrAl 13

ACI Gr. CA 6 NM

Lasposities

Herdrogen

Not required

Analyse

C	Si	Mn	P	S	Cr	Ni	Mo	Nb	Ti	V	N	Fe	W	B	Co	Cu	Al
0.06	0.5	0.6			12.5	4.4	0.5				0.1

Mechanische waarden

Heat Treatment	R_P0,2 (MPa)	Rm (MPa)	A5 (%)	Hardness
Heat Treatment	R_P0,2 (MPa)	Rm (MPa)	A5 (%)	Hardness
As Welded		>760	>15	45 HRc

productblad

prestatieverklaring

conformiteitsverklaring

productblad

Tubular wire based on a 13 Chromium and 4 Nickel deposit for cladding components against corrosion heat and wear resistance

Disclaimer

Whilst all reasonable efforts have been made to ensure the accuracy of the information contained, the information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and any liability incurred from any reliance thereon is expressively disclaimed. Typical data are those obtained when welded and tested in accordance to prescribed standards, and should not be assumed to be the expected results in a particular application or weldment. Other tests and procedures may produce different results. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application. The selection and use of specific products is solely within the control of, and remains the sole responsibility of the customer. The right to change design and/or specifications without notice is reserved.