Type
Tungsten alloyed cored wire for hardfacing applications..

Machinable ,Heat resistant weld deposit with excelent wear resistance. The weld deposit can be heat treated to offer maximum service protection. 

140°C / 2 hr

classification
EN ISO
14700: T Fe3
W.Nr.
1.2567
DIN
MSG 3–GF-45-T
Toepassingen

Rebuilding wornout parts that faces wear and impact combined with increased working temperatures.

Type
Tungsten alloyed cored wire for hardfacing applications..
Toepassingen

Rebuilding wornout parts that faces wear and impact combined with increased working temperatures.

Eigenschappen

Machinable ,Heat resistant weld deposit with excelent wear resistance. The weld deposit can be heat treated to offer maximum service protection. 

Classificatie
EN ISO
14700: T Fe3
W.Nr.
1.2567
DIN
MSG 3–GF-45-T
Geschikt voor

45-52 HRc 

1.2567, 1.2365, 1.2713, 1.2714, 1.2581

30WCrV17 2, 32CrMoV12-283, 55NiCrMoV6, 55NiCrMoV7,  X30WCrV9-3 

Lasposities
PA
PB
Herdrogen

140°C / 2 hr

Hardening : 1060° C-1120° C°, hot bath, compressed air.
Tempering : approx. 3 h / temperature depending on desired working hardness.
Soft annealing : 2 - 4 h at 800° C -840° C / furnace cooling
Gas acc. EN ISO 14175
M13
Analyse
C Si Mn Cr V W Fe
0.3 0.75 0.8 2.5 0.6 4.5 Rem.
Mechanische waarden
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 47 HRc
580°C±15°C 1h 53 HRc