Haynes 617
Weld metal provides optimum strength and oxidation resistance above 816°C (1500°) up to 1149°F (2100°F), especially when welding on base metals of nickel-iron-chromium alloys.
Not required
CEWELD NiCrCo 617 is a high temperature alloy which is used for welding of nickel-chromium-cobalt-molybdenum alloys (UNS Number N06617). This filler metal can also be used for overlay cladding where similar alloy is required such as gas turbines and ethylene equipment.
CEWELD NiCrCo 617 is a high temperature alloy which is used for welding of nickel-chromium-cobalt-molybdenum alloys (UNS Number N06617). This filler metal can also be used for overlay cladding where similar alloy is required such as gas turbines and ethylene equipment.
Weld metal provides optimum strength and oxidation resistance above 816°C (1500°) up to 1149°F (2100°F), especially when welding on base metals of nickel-iron-chromium alloys.
E Ni 6617(NiCr22Co12Mo), ENiCrCoMo-1, 2.4628
2.4608, 2.4663, 2.4851, 1.4876, 1.4859, 1.4952, 1.4958, 1.4959,
NiCr26MoW, NiCr21Co12Mo, NiCr23Co12Mo, NiCr23Fe, X6CrNiNbN 25 20, X5NiCrAlTi 31 20, X8NiCrAlTi 32 21, X10 NiCrAlTi 32 21, GX10 NiCrSiNb 32 20,
UNS: N06601, N06617, N08810, N08811
Inconel Alloys 600 and 601, Incoloy Alloys 800 HT and 802 and cast Alloys such as HK-40, HP and HP-45 Modified, Alloy 617, Alloy 333
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Impact Energy (J) ISO-V | Hardness |
|---|---|---|---|---|---|
| RT | |||||
| As Welded | 480 | 760 | 32 | 120 | HRc |
Lasmetaal biedt optimale sterkte en oxidatieweerstand boven 815 °C (1500 °F) tot 1149 °C (2100 °F), vooral bij het lassen op basismetalen van nikkel-ijzer-chroomlegeringen.
Not required
Lasmetaal biedt optimale sterkte en oxidatieweerstand boven 815 °C (1500 °F) tot 1149 °C (2100 °F), vooral bij het lassen op basismetalen van nikkel-ijzer-chroomlegeringen.
E Ni 6617(NiCr22Co12Mo), ENiCrCoMo-1, 2.4628
2.4608, 2.4663, 2.4851, 1.4876, 1.4859, 1.4952, 1.4958, 1.4959,
NiCr26MoW, NiCr21Co12Mo, NiCr23Co12Mo, NiCr23Fe, X6CrNiNbN 25 20, X5NiCrAlTi 31 20, X8NiCrAlTi 32 21, X10 NiCrAlTi 32 21, GX10 NiCrSiNb 32 20,
UNS: N06601, N06617, N08810, N08811
Inconel Alloys 600 and 601, Incoloy Alloys 800 HT and 802 and cast Alloys such as HK-40, HP and HP-45 Modified, Alloy 617, Alloy 333
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Impact Energy (J) ISO-V | Hardness |
|---|---|---|---|---|---|
| RT | |||||
| As Welded | 480 | 760 | 32 | 120 | HRc |