RE-ON MIG OA622

Ceweld product
Type
Medium -alloyed tubular wire on a C-Cr-Mo-W basis for high hardness up to 550ºC.

Very good abrasion resistance in combination with impact even at higher temperatures up to 550ºC. To much layers should be avoided, preheat is necessary to avoid cracking. A buffer layer with OA 4370 or OA MnCr is recommended in case of sensible basematerial or old layers. Weldable without protective gas. 

140°C / 24 hr

classification
EN ISO
14700: T Fe6
DIN
8555: MF 6-60-PT
Applications

Recommended for parts subject to strong mineral abrasion and erosion, .

Type
Medium -alloyed tubular wire on a C-Cr-Mo-W basis for high hardness up to 550ºC.
Applications

Recommended for parts subject to strong mineral abrasion and erosion, .

Propriétés

Very good abrasion resistance in combination with impact even at higher temperatures up to 550ºC. To much layers should be avoided, preheat is necessary to avoid cracking. A buffer layer with OA 4370 or OA MnCr is recommended in case of sensible basematerial or old layers. Weldable without protective gas. 

Classification
EN ISO
14700: T Fe6
DIN
8555: MF 6-60-PT
Convient pour

HRc 55-58, Cement pumps, crusher bars, hammer and blooming table rolls, mineral and brick industry.

Positions de soudage
PA
PB
Etuvage

140°C / 24 hr

Analyse
C Si Mn Cr Ni Mo Nb Ti V N Fe W B Co Cu Al
0.55 0.9 2.8 7 1.6 1.8 Rem. 0.9
Propriétés mécaniques
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 55 HRc