AX-450W
Masivdraht
Ceweld product
Type
Tungsten alloyed cored wire for hardfacing applications..
Machinable ,Heat resistant weld deposit with excelent wear resistance. The weld deposit can be heat treated to offer maximum service protection.
140°C / 2 hr
classification
EN ISO
14700: T Fe3
W.Nr.
1.2567
DIN
MSG 3–GF-45-T
Applications
Rebuilding wornout parts that faces wear and impact combined with increased working temperatures.
Type
Tungsten alloyed cored wire for hardfacing applications..
Applications
Rebuilding wornout parts that faces wear and impact combined with increased working temperatures.
Propriétés
Machinable ,Heat resistant weld deposit with excelent wear resistance. The weld deposit can be heat treated to offer maximum service protection.
Classification
EN ISO
14700: T Fe3
W.Nr.
1.2567
DIN
MSG 3–GF-45-T
Convient pour
45-52 HRc
1.2567, 1.2365, 1.2713, 1.2714, 1.2581
30WCrV17 2, 32CrMoV12-283, 55NiCrMoV6, 55NiCrMoV7, X30WCrV9-3
Positions de soudage
Hardening : 1060° C-1120° C°, hot bath, compressed air.
Tempering : approx. 3 h / temperature depending on desired working hardness.
Soft annealing : 2 - 4 h at 800° C -840° C / furnace cooling
Tempering : approx. 3 h / temperature depending on desired working hardness.
Soft annealing : 2 - 4 h at 800° C -840° C / furnace cooling
Gas acc. EN ISO 14175
M13
Propriétés mécaniques
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| As Welded | 47 HRc | |||
| 580°C±15°C 1h | 53 HRc |