UTP A Celsit 706 V

Brand
UTP
Ceweld product
Type
Cobalt-based thermo shock resistant alloy for overlay applications. (Stellite 6)
classification
AWS
A 5.21: ERCoCr-A
EN ISO
14700: S Co2
Applications

Steam-valves, high temperature liquid pumps, hot cutting tools, exhaust valves.

Type
Cobalt-based thermo shock resistant alloy for overlay applications. (Stellite 6)
Applications

Steam-valves, high temperature liquid pumps, hot cutting tools, exhaust valves.

Properties

Outstanding alloy against abrasion, thermo-shock and corrosion combined with high temperatures. The weld deposit can be machined with tungsten tool tips and by grinding. The hardness of the weld deposit will degrees 16% at 300°C and about 30% at 600°C. The weld deposit is high heat resistant up to 900°C. DUR 6 offers a low coefficient of friction of 0.12 and exceptional resistance to galling. It has cavitation-erosion resistance ten times that of 304 stainless steel, DUR 6 can be used to protect bearing surfaces in non-lubricating conditions due to its resistance to metal-to-metal wear. 

Classification
AWS
A 5.21: ERCoCr-A
EN ISO
14700: S Co2
F-nr
71
Suitable for

Stellite 6 alloy for, Steam-valves, high temperature liquid pumps, hot cutting tools, exhaust valves and seats

Welding positions
PA
PB
PC
Redrying
Not required
Gas acc. EN ISO 14175
I1
Analysis
C Si Mn Cr Ni Mo V Fe W B Co Nb Cu Al Ti N
1.1 1 0.6 28 2.5 5 Rem.
Mechanical Properties
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 40 HRc
Product sheet
MSDS
product sheet
Ask quotation
MSDS
Type
Cobalt based (Stellite 6) fluxcored welding wire (FCAW) for overlay welding.
classification
AWS
A 5.21: ERCoCr-A
EN ISO
14700: T Co2
DIN
8555: MSG 20-GF-40-CTZ
Applications

Cladding valves, Steam-valves, high temperature liquid pumps, hot cutting tools, exhaust valves, seats, cutting knives, metal to metal wear, bearing surfaces, chemical industry, hot shear blades etc. Cladding valves, Steam-valves, high temperature liquid pumps, hot cutting tools, exhaust valves, seats, cutting knives, metal to metal wear, bearing surfaces, chemical industry, hot shear blades etc.

Type
Cobalt based (Stellite 6) fluxcored welding wire (FCAW) for overlay welding.
Applications

Cladding valves, Steam-valves, high temperature liquid pumps, hot cutting tools, exhaust valves, seats, cutting knives, metal to metal wear, bearing surfaces, chemical industry, hot shear blades etc. Cladding valves, Steam-valves, high temperature liquid pumps, hot cutting tools, exhaust valves, seats, cutting knives, metal to metal wear, bearing surfaces, chemical industry, hot shear blades etc.

Properties

Outstanding alloy against abrasion, thermo-shock and corrosion combined with high temperatures. The weld deposit can be machined with tungsten tool tips and by grinding. The hardness of the weld deposit will degrease 16% at 300°C and about 30% at 600°C. Excellent alloy against thermal shock, abrasion, erosion, corrosion and cavitation at high temperature.

Classification
AWS
A 5.21: ERCoCr-A
EN ISO
14700: T Co2
F-nr
71
DIN
8555: MSG 20-GF-40-CTZ
Suitable for

ER CoCr-A 

Stellite 6

Celist 706

Welding positions
PA
PB
PC
Redrying
140°C / 24 hr
Gas acc. EN ISO 14175
M13
Analysis
C Si Mn Cr Ni Mo V Fe W B Co Nb Cu Al Ti N
1 1 0.8 28 2 0.01 3 4.5 Rem.
Mechanical Properties
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 43 HRc