Type
Medium -alloyed tubular wire on a C-Cr-Mo-W-V basis for high hardness up to 550ºC.

Very good abrasion resistance in combination with impact even at higher temperatures up to 550ºC. To much layers should be avoided, preheat is necessary to avoid cracking. A buffer layer with OA 4370 or OA MnCr is recommended in case of sensible base material or old layers. Weldable without protective gas.

140°C / 24 hr

classification
EN ISO
14700: T Fe6
Anwendungen

Recommended for parts subject to strong mineral abrasion and erosion.

Type
Medium -alloyed tubular wire on a C-Cr-Mo-W-V basis for high hardness up to 550ºC.
Anwendungen

Recommended for parts subject to strong mineral abrasion and erosion.

Eigenschaften

Very good abrasion resistance in combination with impact even at higher temperatures up to 550ºC. To much layers should be avoided, preheat is necessary to avoid cracking. A buffer layer with OA 4370 or OA MnCr is recommended in case of sensible base material or old layers. Weldable without protective gas.

Klassifikation
EN ISO
14700: T Fe6
Geeignet für

Cement pumps, Crusher bars, Hammer and Blooming table rolls, Mineral and Brick industry.

Schweißpositionen
PA
PB
PC
Rücktrocknung

140°C / 24 hr

Analyse
C Si Mn Cr Ni Mo Nb Ti V N Fe W B Co Cu Al
0.55 1 2.7 6.7 1.6 1.5 Rem. 1
Mechanische Gütewerte
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 60 HRc