- Produktspezifikationen
- Verpackung
- Bitte um Angebot
Type
Medium -alloyed seamless fluxcored wire on a C-Cr-Mo-W-V basis offering high hardness up to 500ºC.
Very good abrasion resistance in combination with impact even at higher temperatures up to 500ºC. To much layers should be avoided, preheat is necessary to avoid cracking. A buffer layer with AA M690 or AA M37-42 is recommended in case of sensible base material or old hardfacing layers.
Not required
classification
AWS
A 5.21: ERFe-8
EN ISO
14700: T Fe8
W.Nr.
~1.2606
DIN
MSG 3-GF-60-GPZ
Anwendungen
Recommended for parts subject to strong mineral abrasion and erosion that faces increased working temperatures up to 500°C.
Type
Medium -alloyed seamless fluxcored wire on a C-Cr-Mo-W-V basis offering high hardness up to 500ºC.
Anwendungen
Recommended for parts subject to strong mineral abrasion and erosion that faces increased working temperatures up to 500°C.
Eigenschaften
Very good abrasion resistance in combination with impact even at higher temperatures up to 500ºC. To much layers should be avoided, preheat is necessary to avoid cracking. A buffer layer with AA M690 or AA M37-42 is recommended in case of sensible base material or old hardfacing layers.
Klassifikation
AWS
A 5.21: ERFe-8
EN ISO
14700: T Fe8
W.Nr.
~1.2606
DIN
MSG 3-GF-60-GPZ
Geeignet für
HRc 58-62, Cement pumps, crusher bars, hammer and blooming table rolls, mineral and brick industry, stone crushers.
Schweißpositionen
Gas acc. EN ISO 14175
M21
Mechanische Gütewerte
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| As Welded | 59 HRc |