Haynes 718
Special alloy with age hardenable deposit and similar mechanical properties as the base metal. Age hardened condition: 720ºC for 8 Hours, furnace Cool 55ºC/ hour to 620ºC, than Air Cool for 8 hours.
Not required
CEWELD® NiCro 718 is used in a wide range of applications such as components for liquid fueled rockets, rings, casings and various formed sheet metal parts for aircraft and land-based gas turbine engines, and cryogenic tankage.
It is also used for fasteners and instrumentation parts.
718 filler metal can be also used for cladding and overlay of parts in the oil and gas industry.
CEWELD® NiCro 718 is used in a wide range of applications such as components for liquid fueled rockets, rings, casings and various formed sheet metal parts for aircraft and land-based gas turbine engines, and cryogenic tankage.
It is also used for fasteners and instrumentation parts.
718 filler metal can be also used for cladding and overlay of parts in the oil and gas industry.
Special alloy with age hardenable deposit and similar mechanical properties as the base metal. Age hardened condition: 720ºC for 8 Hours, furnace Cool 55ºC/ hour to 620ºC, than Air Cool for 8 hours.
Cr-Ni-Nb-Mo alloy and 718, 706, and X-750 alloys.
EN W.Nr.: 2.4668 (NiCr19Fe19Nb5Mo3), 2.4669 (NiCr15Fe7TiAl).
ASTM: B637, 5589.
UNS: N07718, N09706, N07750.
Inconel 718(2.4668), 706 and X-750 (X750)
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| As Welded | 580 | 860 | 28 | HRc |
Special alloy with age hardenable deposit and similar mechanical properties as the base metal. Age hardened condition: 720ºC for 8 Hours, furnace Cool 55ºC/hour to 620ºC than Air Cool for 8 hours
Not required
CEWELD NiCro 718 is used in a wide range of applications such as components
for liquid fueled rockets, rings, casings and various formed sheet metal
parts for aircraft and land-based gas turbine engines, and cryogenic tankage.
It is also used for fasteners and instrumentation parts.
718 filler metal can be also used for cladding and overlay of parts
in the oil and gas industry.
CEWELD NiCro 718 is used in a wide range of applications such as components
for liquid fueled rockets, rings, casings and various formed sheet metal
parts for aircraft and land-based gas turbine engines, and cryogenic tankage.
It is also used for fasteners and instrumentation parts.
718 filler metal can be also used for cladding and overlay of parts
in the oil and gas industry.
Special alloy with age hardenable deposit and similar mechanical properties as the base metal. Age hardened condition: 720ºC for 8 Hours, furnace Cool 55ºC/hour to 620ºC than Air Cool for 8 hours
Inconel 718(2.4668), 706 and X-750 (X750)
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| As Welded | 580 | 860 | 28 | HRc |